COLD FORMING MATERIALS

Kawat C10E2C CHQ

MATERIALSENGINEERINGCREATION GROUP

Pusat Produk / Piawaian ISO / ISO 4954-lampiran B

Kawat C10E2C CHQ

Diameter: 0.40-46mm

Kekuatan tegangan: Rujuk maklumat teknikal

Product Detail Technical Information Inspection Packaging

Shanghai Creation GroupAdalah perusahaan penanda aras yang memberi tumpuan kepada dawai keluli berkualiti tinggi di China. Pasukan pengurusan keseluruhan mempunyai 20 tahun pengalaman dalam industri. Kami membina hubungan yang baik dengan banyak pembekal tier 1 kepada industri automotif, semua rod dawai diperoleh daripada kilang keluli berjenama. Semua pesanan adalah 100% dikesan.

Keadaan penghantaran

: +AR atau +PE

: +AC atau +AC+PE

: +AR+C

: +AR+C+AC

: +AR+C+AC+LC

: +AC+C

Kualiti permukaan

- : Berterusan dan lancar

- : Percuma lipit, bertindih, lubang, calar dan parut lukisan

- : Percuma karat

Permohonan

- : Industri automobil

- : Industri pembinaan

- : Industri jentera

- : Industri-industri lain

Kajian kes

Products & Service

Rod dawai keluli

Penjerukan asid dan pemfosfatan

Penarikan sejuk

Penyepuhlindapan pensferaan

Pemeriksaan

Produk siap

1. Gabungan terma penghantaran

Jadual B.1-gabungan keadaan rawatan haba pada penghantaran, bentuk produk dan keperluan yang berkenaan

Heat-treatment condition at delivery	Symbol	Products form a			Applicable requirements in cases where the steel concerned has been ordered with reference to the steel names indicated in
Heat-treatment condition at delivery	Symbol	Wire rod	Bar	Wire	TablesB.2,B.3,B.4 or B.5		TablesB.2,B.3,B.4,B.5,B.6 or B,7			Optional
As hot-rolled or peeled	+AR or +PE	X	X	X	Chemical composition as specified in Table B.2	Mechanical properties as specified in TablesB.3,B.4 and B.5	Chemical compositior as specified in Table B.2	Mechanical properties as specified inTablesB,3,B.4 and B.5	Values for hardenability according to Tables B.6 and B.7	Supplementa- ry or special requirements as specified in Annex Eh
Cold drawn	+AR+C	-	X	X
Cold drawn + spheroidized	+AR+C+AC	-	X	X
Cold drawn + spheroidized+skin passed	+AR+C+AC +LC	-	X	X
Spheroidized or spheroidized+peeled	+AC or +AC +PE	X	X	X
Spheroidized+cold drawn	+AC+C		X	X
Treated to ferrite- pearlite structure and hardness range	+FP	-	X	-
Others	Other delivery conditions may be agreed at the time of ordering
a X=applicable,-=not applicable. b If agreed at the time of the enquiry and order.

2. Komposisi kimia

Jadual B.2-komposisi kimia (berkenaan dengan analisis cast) keluli untuk pengerasan kes

Steel name b	% mass fraction a
Steel name b	C	Si c	Mn	P	S	Cr	Ni	Mo	B	Cu
Non-alloy steel grades
C10E2C	0,08 to 0,12	0,30	0,30 to 0,60	0,025	0,025		—		—	0,25
C15E2C	0,13 to 0,17	0,30	0,30 to 0,60	0,025	0,025		—	—	—	0,25
C17E2C	0,15 to 0,19	0,30	0,60 to 0,90	0,025	0,025		—	—	—	0,25
C20E2C	0,18 to 0,22	0,30	0,30 to 0,60	0,025	0,025	—	—		—	0,25
Alloy steel grades
18MnB4	0,16 to 0,20	0,30	0,90 to 1,20	0,025	0,025		—	—	0,0008 to 0,005	0,25
22MnR4	0,20 to 0,24	0,30	0,90 to 1,20	0,025	0,025	——	—	—	0,0008 to 0,005	0,25
17Cr3	0,12 to 0,20	0,30	0,60 to 0,90	0,025	0,025	0,70 to 1,25	—	—	—	0,25
17CrS3	0,12 to 0,20	0,30	0,60 to 0,90	0,025	0,020 to 0,040	0,70 to 1,25	—	—	—	0,25
20Cr4	0,17 to 0,23	0,30	0,60 to 0,90	0,025	0,025	0,90 to 1,20	—	—	—	0,25
20CrS4	0,17 to 0,23	0,30	0,60 to 0,90	0,025	0,020 to 0,040	0,90 to 1,20	—	—	—	0,25
16MnCr5	0,14 to 0,19	0,30	1,00 to 1,30	0,025	0,025	0,80 to 1,10		—	—	0,25
16MnCrS5	0,14 to 0,19	0,30	1,00 to 1,30	0,025	0,020 to 0,040	0,80 to 1,10	—	—		0,25
16MnCrB5	0,14 to 0,19	0,30	1,00 to 1,30	0,025	0,025	0,80 to 1,10	—	—	0,0008 to 0,005	0,25
20MnCrS5	0,17 to 0,22	0,30	1,10 to 1,40	0,025	0,020 to 0,040	1,00 to 1,30	—	—	—	0,25
12CrMo4	0,10 to 0,15	0,30	0,60 to 0,90	0,025	0,025	0,90 to 1,20	—	0,15 to 0,25	—	0,25
18CrMo4	0,15 to 0,21	0,30	0,60 to 0,90	0,025	0,025	0,90 to 1,20	—	0,15 to 0,25	—	0,25
18CrMoS4	0,15 to 0,21	0,30	0,60 to 0,90	0,025	0,020 to 0,040	0,90 to 1,20	—	0,15 to 0,25	—	0,25
20MoCr4	0,17 to 0,23	0,30	0,70 to 1,00	0,025	0,025	0,30 to 0,60		0,40 to 0,50		0,25
20MoCrS4	0,17 to 0,23	0,30	0,70 to 1,00	0,025	0,020 to 0,040	0,30 to 0,60	—	0,40 to 0,50	—	0,25
Elements not quoted in this table should not be intentionally added to the steel without the agreement of the purchaser,except those intended for finishing the heat.All reasonable precautions shall be taken in order to prevent the addition of such elements from scrap or other materials used in the production process,which can affect the hardenability, mechanical properties and applicability To improve the performance of cold heading,it is possible to add Al:0,020 %to 0,050 % a Maximum values unless otherwise indicated. b In the case of steels with hardenability requirements (see Tables B.6 and B.Z),minor deviations from the specified limits are permitted (with the exception of sulfur and phosphorus),provided that they do not exceed 0,01 %for carbon and the values indicated in Table 2 for the other elements. c A lower silicon content or a specific silicon range may be agreed at the time of ordering

Steel name b	% mass fraction a
Steel name b	C	Si c	Mn	P	S	Cr	Ni	Mo	B	Cu
10NiCr5-4	0,07 to 0,12	0,30	0,60 to 0,90	0,025	0,025	0,90 to 1,20	1,20 to 1,50			0,25
12NiCr3-2	0,09 to 0,15	0,30	0,30 to 0,60	0,025	0,025	0,40 to 0,70	0,50 to 0,80	—		0,25
17CrNi6-6	0,14 to 0,20	0,30	0,50 to 0,90	0,025	0,025	1,40 to 1,70	1,40 to 1,70			0,25
20NiCrMo2-2	0,17 to 0,23	0,30	0,65 to 0,95	0,025	0,025	0,35 to 0,70	0,40 to 0,70	0,15 to 0,25		0,25
20NiCrMoS2-2	0,17 to 0,23	0,30	0,65 to 0,95	0,025	0,020 to 0,040	0,35 to 0,70	0,40 to 0,70	0,15 to 0,25	—	0,25
20NiCrMo7	0,17 to 0,23	0,30	0,40 to 0,70	0,025	0,025	0,35 to 0,65	1,60 to 2,00	0,20 to 0,30		0,25
20NiCrMoS6-4	0,16 to 0,23	0,30	0,50 to 0,90	0,025	0,020 to 0,040	0,60 to 0,90	1,40 to 1,70	0,25 to 0,35	—	0,25
Elements not quoted in this table should not be intentionally added to the steel without the agreement of the purchaser,except those intended for finishing the heat.All reasonable precautions shall be taken in order to prevent the addition of such elements from scrap or other materials used in the production process,which can affect the hardenability, mechanical properties and applicability To improve the performance of cold heading,it is possible to add Al:0,020 %to 0,050 % a Maximum values unless otherwise indicated. b In the case of steels with hardenability requirements (see TablesB.6 and B.7),minor deviations from the specified limits are permitted (with the exception of sulfur and phosphorus),provided that they do not exceed 0,01 %for carbon and the values indicated in Table 2 for the other elements. c A lower silicon content or a specific silicon range may be agreed at the time of ordering.

3. Sifat-sifat mekanikal

Jadual B.3-sifat mekanikal gred keluli bukan aloi

Steel name	Diameter		Delivery condition
	Diameter		+AR or+PE		+AC or+AC+PE		+AR+C		+AR+C+AC		+AR+C+AC+LC		+AC+C
	above mm	up to mm	Rm max. MPa	Za min. %	Rm max MPa	Z min. %	Rm max. MPa	Z min. %	Rm max MPa	Z min. %	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %
C10E2C	2	5	—		—	—	—	—	390	67	430	65	—	—
	5	10	450	58	400	65	540	56	380	67	420	65	490	62
	10	40	450	58	400	65	530	56	380	67	420	65	480	62
	40	100	450	58	400	65		—					——
C15E2C	2	5							420	67	460	65
	5	10	480	58	430	65	570	56	410	67	450	65	520	62
	10	40	480	58	430	65	560	56	410	67	450	65	510	62
	40	100	480	58	430	65	—	—	—			—	——
C17E2C	2	5	——	—	—	—	——		440	67	480	65	—	—
	5	10	530	58	450	65	630	56	430	67	470	65	550	62
	10	40	530	58	450	65	620	56	430	67	470	65	540	62
	40	100	530	58	450	65	—		—	—	—	—	——	—
C20E2C	2	5				—	—		460	67	500	65
	5	10	530	58	470	65	640	56	450	67	490	65	580	62
	10	40	530	58	470	65	630	56	450	67	490	65	570	62
	40	100	530	58	470	65	—	—		一	—	——	——	—
a The values are given only for information.